Sisitemu z’imiti zikoresha umwuka ushyushye zirimo moteri zitanga amashanyarazi, valve zo kugenzura, imiyoboro cyangwa imiyoboro ikwirakwiza amazi, imitego ikoresha thermodynamic cyangwa equilibrium thermostatic traps, pressure gauges, pressure reduction, valves defensive, na volumetric accumulators.
Ibice byinshi muri ibi bikozwe mu cyuma kitagira umugese cya litiro 316 kandi birimo gasket za fluoropolymer (ubusanzwe polytetrafluoroethylene, izwi kandi nka Teflon cyangwa PTFE), hamwe n'ibikoresho bya semi-metal cyangwa ibindi bikoresho bya elastomeric.
Ibi bice bishobora kwangirika cyangwa kwangirika mu gihe cyo kubikoresha, ibyo bikaba bigira ingaruka ku bwiza bw'ibikoresho bya Clean Steam (CS). Uyu mushinga wasobanuwe muri iyi ngingo wasuzumye ingero z'ibyuma bitanduye byavuye mu bushakashatsi bune bwa CS, wasuzumye ingaruka zishobora guterwa n'ingaruka ku mikorere n'imikorere y'ikoranabuhanga, kandi wagerageje uduce duto n'ibyuma biri muri condensate.
Ingero z'ibice by'imiyoboro yangiritse n'ibice by'uburyo bwo gukwirakwiza amazi bishyirwa kugira ngo harebwe ibyavuye mu kwangirika. 9 Kuri buri kibazo cyihariye, hasuzumwe imiterere itandukanye y'ubuso. Urugero, hasuzumwe ingaruka zisanzwe zo kwijima no kwangirika.
Ubuso bw'ibipimo byagaragajwe bwapimwe kugira ngo harebwe niba hari ibisebe by'amabara y'urubura hakoreshejwe uburyo bwo kugenzura amaso, Auger electron spectroscopy (AES), electron spectroscopy yo gusesengura ibinyabutabire (ESCA), scanning electron microscopy (SEM) na X-ray photoelectron spectroscopy (XPS).
Ubu buryo bushobora kugaragaza imiterere ifatika n'iy'atome ya kwangirika n'ibisigazwa, ndetse no kugena ibintu by'ingenzi bigira ingaruka ku miterere y'ibinyabutabire bya tekiniki cyangwa ibicuruzwa bya nyuma.
Ibikoresho byangiritse by’icyuma kitagira umugese bishobora kugira imiterere myinshi, urugero nk’urukuta rwa carmine rwa oxide y’icyuma (umukara cyangwa umutuku) hejuru y’urukuta rwa oxide y’icyuma (umukara cyangwa imvi)2. Ubushobozi bwo kugenda bugana hepfo.
Urusobe rw'icyuma cya okiside (umukara w'umukara) rushobora kwiyongera uko igihe kigenda gihita uko ibisigazwa bigenda bigaragara cyane, nk'uko bigaragazwa n'uduce cyangwa ibisigazwa bigaragara ku buso bw'icyumba cyo gusukura no ku bikoresho cyangwa ibikoresho nyuma yo gusukura umwuka, habaho kwimuka. Isesengura rya laboratwari ry'ibipimo bya condensate ryagaragaje imiterere y'ibisigazwa n'ingano y'ibyuma bishongesha mu mazi ya CS.
Nubwo hari impamvu nyinshi zitera iki kibazo, icyuma gitanga amashanyarazi cya CS akenshi ni cyo gikunze kugira uruhare runini. Ni ibisanzwe kubona okiside y'icyuma itukura (umukara/umutuku) ku buso na okiside y'icyuma (umukara/umukara) mu myobo inyura buhoro buhoro muri sisitemu yo gukwirakwiza CS. 6
Sisitemu yo gukwirakwiza CS ni imiterere y'amashami ifite ingingo nyinshi zo gukoresha zirangira mu bice bya kure cyangwa ku mpera y'umutwe mukuru n'imitwe mito itandukanye y'amashami. Sisitemu ishobora kuba irimo uburyo bwinshi bwo kugenzura kugira ngo ifashe gutangiza kugabanya umuvuduko/ubushyuhe ahantu runaka hashobora kuba hari ingingo zishobora kwangirika.
Ingese ishobora no kubaho mu mitego y’isuku ishyirwa ahantu hatandukanye muri sisitemu kugira ngo ikuremo umwuka uvanze n’amazi meza unyura mu mutego, mu miyoboro inyuramo/isohoka cyangwa umutwe w’amazi uvanze n’amazi.
Akenshi, kwimuka inyuma y’amazi birashoboka aho ingese ziyongera ku mutego zikazamuka zijya mu miyoboro yegereye cyangwa mu miyoboro ikoreshwa; ingese zigaragara mu mitego cyangwa ibindi bice zishobora kugaragara hejuru y’isoko hamwe n’izamuka rihoraho.
Bimwe mu bice by'icyuma kitagira umugese nabyo bigaragaza imiterere itandukanye y'icyuma iciriritse kugeza ku rwego rwo hejuru, harimo na delta ferrite. Bivugwa ko kristu za ferrite zigabanya ubudahangarwa bw'ingufu, nubwo zishobora kuba ziri hagati ya 1–5%.
Ferrite kandi ntabwo irwanya ingese nk'imiterere ya kristu ya austenitic, bityo izangirika cyane. Ferrite zishobora kumenyekana neza hakoreshejwe probe ya ferrite kandi zigafatwa neza hakoreshejwe magnet, ariko hari imbogamizi zikomeye.
Kuva ku gushyiraho sisitemu, kugeza ku gutangira gukora, no gutangiza icyuma gishya cya CS generator n'imiyoboro ikwirakwiza, hari ibintu byinshi bigira uruhare mu kwangirika:
Uko igihe kigenda gihita, ibintu nk'ibi bishobora gukora ibintu byangiritse iyo bihuye, bivanze, kandi bihurirana n'ibivanze by'icyuma n'icyuma. Ubusanzwe ivu ry'umukara riboneka mbere na mbere muri generator, hanyuma rikagaragara mu miyoboro isohora amashanyarazi ndetse amaherezo rigakwirakwira muri sisitemu yo gukwirakwiza amashanyarazi ya CS.
Isesengura rya SEM ryakozwe kugira ngo hagaragazwe imiterere y’ibikomoka ku kwangirika bitwikiriye ubuso bwose hakoreshejwe kristu n’ibindi bice. Inyuma cyangwa ubuso bw’inyuma aho ibice biboneka hatandukanye kuva ku byiciro bitandukanye by’icyuma (Ishusho ya 1-3) kugeza ku bipimo bisanzwe, ari byo silica/icyuma, umusenyi, vitreous, deposits zihuye (Ishusho ya 4). Imiyoboro y’umwuka nayo yasesenguwe (Ishusho ya 5-6).
Ikizamini cya AES ni uburyo bwo gusesengura bukoreshwa mu kumenya ubuziranenge bw'icyuma kidashonga no gusuzuma ubukana bwacyo bwo kwangirika. Bugaragaza kandi kwangirika kwa firime idashonga no kugabanuka k'ubwinshi bwa chromium muri firime idashonga uko ubuso bugenda burushaho kwangirika bitewe na firime.
Kugira ngo hamenyekane imiterere y’ibice by’ubuso bwa buri gipimo, hakoreshejwe uburyo bwa AES scan (imiterere y’ibice by’ubuso hejuru y’ubujyakuzimu).
Buri hantu hakoreshwa mu gusesengura no kongera SEM hatoranijwe neza kugira ngo hatange amakuru aturutse mu turere dusanzwe. Buri bushakashatsi bwatanze amakuru aturutse ku bice bike bya molekile byo hejuru (bigereranyijwe kuri angstroms 10 [Å] kuri buri gice) kugeza ku bujyakuzimu bw'icyuma (200–1000 Å).
Ingano nini y'icyuma (Fe), chromium (Cr), nikeli (Ni), ogisijeni (O) na karuboni (C) yanditswe mu turere twose twa Rouge. Amakuru ya AES n'ibyavuye mu bushakashatsi byagaragajwe mu gice cy'inyigo.
Ibisubizo rusange bya AES ku miterere y’ibanze bigaragaza ko ogisijeni ikomeye ibaho ku bipimo bifite ubunini budasanzwe bwa Fe na O (okiside z’icyuma) hamwe n’ingano nto ya Cr ku buso. Uku gushonga k’umutuku bituma hasohoka uduce dushobora kwanduza umusaruro n’ubuso buhuye n’umusaruro.
Nyuma yo gukuraho ubururu, ingero za "passivated" zagaragaje ko filime idakora neza yagarutse, aho Cr yageze ku rugero rwo hejuru kurusha Fe, hamwe n'igipimo cy'ubuso cya Cr:Fe kiri hagati ya 1.0 na 2.0 kandi nta oxide y'icyuma muri rusange ihari.
Ubuso butandukanye bw’ibinure bwasesenguwe hakoreshejwe XPS/ESCA kugira ngo hagereranywe ibipimo by’ibinyabutabire n’imiterere ya okiside ya spectral ya Fe, Cr, sulfur (S), kalisiyumu (Ca), sodium (Na), fosifore (P), azote (N), na O. na C (imbonerahamwe A).
Hari itandukaniro rigaragara mu bipimo bya Cr uhereye ku gaciro kari hafi y’urwego rwa passivation kugeza ku gaciro ko hasi gasanzwe kaboneka mu byuma by’ibanze. Ingano y’icyuma na chromium biboneka ku buso igaragaza ubunini butandukanye n’ibyiciro bitandukanye by’ibice bya rouge. Ibipimo bya XPS byagaragaje ubwiyongere bwa Na, C cyangwa Ca ku buso butoshye ugereranije n’ubuso busukuwe n’ubuto buto.
Isuzuma rya XPS ryagaragaje kandi urugero rwo hejuru rwa C mu ibara ry'umutuku w'icyuma (umukara) ndetse na Fe(x)O(y) (icyuma oxide) mu ibara ry'umutuku. Amakuru ya XPS ntabwo ari ingirakamaro mu gusobanukirwa impinduka zo ku buso mu gihe cyo kwangirika kuko asuzuma icyuma gitukura n'icyuma cy'ibanze. Hakenewe isuzuma ryinshi rya XPS hakoreshejwe ingero nini kugira ngo hasuzumwe neza ibisubizo.
Abanditsi ba mbere nabo bagize ikibazo cyo gusuzuma amakuru ya XPS. Ibyagaragaye mu gihe cyo gukuraho byagaragaje ko karuboni nyinshi kandi akenshi ikurwaho hakoreshejwe uburyo bwo kuyungurura mu gihe cyo gutunganya. Imikorobe za SEM zafashwe mbere na nyuma yo gukuraho iminkanyari zigaragaza ibyangiritse ku buso biterwa n'ibi bisigazwa, harimo n'ibice n'imyenge, bigira ingaruka ku buryo butaziguye ku ingese.
Ibisubizo bya XPS nyuma yo kudakoresha neza byagaragaje ko igipimo cya Cr:Fe ku buso cyari hejuru cyane ubwo filime yo kudakoresha neza yasubirwagamo, bityo bigabanya umuvuduko wa corruption n'izindi ngaruka mbi ku buso.
Ingero za coupon zagaragaje ukwiyongera gukomeye kw'igipimo cya Cr:Fe hagati y'ubuso "uko buri" n'ubuso budafite umwuka. Igipimo cya mbere cya Cr:Fe cyageragejwe hagati ya 0.6 na 1.0, mu gihe igipimo cya nyuma yo kuvurwa cyari hagati ya 1.0 na 2.5. Agaciro k'ibyuma bitagira umugese byahinduwe n'amashanyarazi n'ibidafite umwuka biri hagati ya 1.5 na 2.5.
Mu bipimo byakoreweho isuzuma nyuma yo gutunganya, uburebure ntarengwa bw'igipimo cya Cr:Fe (cyashyizweho hakoreshejwe AES) bwari hagati ya 3 na 16 Å. Bigereranywa neza n'amakuru yavuye mu bushakashatsi bwakozwe mbere na Coleman2 na Roll. 9 Ubuso bw'ibipimo byose bwari bufite urugero rusanzwe rwa Fe, Ni, O, Cr, na C. Urugero ruri hasi rwa P, Cl, S, N, Ca, na Na narwo rwabonetse muri byinshi muri ibyo bipimo.
Ibi bisigazwa ni ibisanzwe mu byuma bisukura imiti, amazi meza, cyangwa electropolishing. Nyuma yo gusesengura, hagaragaye ubwandu bwa silikoni ku buso no ku rwego rutandukanye rwa kristu ya austenite ubwayo. Inkomoko isa nkaho ari silika iri mu mazi/umwuka, polishing ya mekanike, cyangwa ikirahuri cyashongeshejwe cyangwa cyashushanyijwe mu karemangingo ka CS.
Ibicuruzwa byangiritse biboneka muri sisitemu za CS bivugwa ko bitandukanye cyane. Ibi biterwa n'imiterere itandukanye y'izi sisitemu ndetse n'aho ibice bitandukanye nk'amavali, imitego n'ibindi bikoresho bishobora gutera imiterere yangiritse n'ibicuruzwa byangiritse.
Byongeye kandi, ibice bisimbura ibindi bikunze gushyirwa muri sisitemu bitarakoreshwa neza. Ibikoresho byangiritse nabyo bigira ingaruka zikomeye ku miterere ya moteri ya CS n'ubwiza bw'amazi. Ubwoko bumwe na bumwe bwa moteri ni ibyuma bishyushya amazi mu gihe ubundi ari ibyuma bishyushya amazi. Moteri za CS zikoresha ecran zo gukuraho ubushuhe mu mwuka mwiza, mu gihe izindi moteri zikoresha imirasire cyangwa umuyaga.
Hari aho ibumba ry’icyuma risa n’aho rikomeye mu muyoboro w’amazi n’icyuma gitukura gitwikira. Ibumba ridafite aho rihuriye rikora agace k’icyuma k’umukara gafite agahu k’icyuma gafite ubururu bw’icyuma munsi maze rigakora ikindi kintu cyo hejuru mu buryo bw’ubururu bw’umuswa bworoshye guhanagura ku buso.
Nk’uko bisanzwe, iyi miyoboro isa n’ifu igaragara cyane kurusha iy’icyuma gitukura, kandi igendagenda cyane. Bitewe n’ubwiyongere bw’imiterere y’icyuma mu gifu, igifu cyakorewe mu muyoboro wa fumbire uri hepfo y’umuyoboro ukwirakwiza amazi gifite igifu cya fumbire hejuru y’igifu.
Ubururu bw'icyuma bunyura mu gikoresho gikusanya ubururu, bugaragara mu muyoboro w'amazi, kandi urwego rwo hejuru rushobora gukurwaho byoroshye. Ubwiza bw'amazi bugira uruhare runini mu miterere y'ubururu.
Ingano nyinshi ya hydrocarbon ituma habaho ivu ryinshi mu minwa, mu gihe ingano nyinshi ya silika ituma habaho ingano nyinshi ya silika, bigatuma uruhu rworoshye cyangwa rubengerana. Nkuko byavuzwe mbere, indorerwamo zo mu mazi nazo zishobora kwangirika, bigatuma imyanda na silika byinjira muri sisitemu.
Imbunda ni ikibazo gikomeye mu buryo bw'umwuka kuko ibice binini bishobora gukora ibice binini. Ibi bice biboneka ku buso bw'umwuka cyangwa mu bikoresho byo gusukura umwuka. Ibice bikurikira bivuga ingaruka zishobora guterwa n'imiti.
Ishusho ya As-Is SEMs iri ku Ishusho ya 7 na 8 igaragaza imiterere ya microcrystalline ya carmine yo mu cyiciro cya 2 mu rubanza rwa 1. Matrix ikomeye cyane ya crystals za fer oxide yakozwe ku buso mu buryo bw'ibisigazwa byoroheje. Ubuso bwanduye n'ubudahangarwa bwagaragaje kwangirika kwa corruption bigatuma ubuso bugoramye kandi bufite imyenge mike nk'uko bigaragara ku Ishusho ya 9 na 10.
Isuzuma rya NPP riri ku ishusho ya 11 rigaragaza imiterere y'ibanze y'ubuso bw'umwimerere bufite oxide y'icyuma iremereye kuri bwo. Ubuso budafite imbaraga n'ubudafite ingufu (Ishusho ya 12) bwerekana ko filime idakoresha imbaraga ubu ifite Cr (umurongo utukura) iri hejuru y'umurongo wa Fe (umurongo w'umukara) kuri > 1.0 Cr:Fe ratio. Ubuso budafite imbaraga n'ubudafite ingufu (Ishusho ya 12) bwerekana ko filime idakoresha imbaraga ubu ifite Cr (umurongo utukura) iri hejuru y'umurongo wa Fe (umurongo w'umukara) kuri > 1.0 Cr:Fe ratio. Пасси новов ояя һәм обесточенная поверхность (рис. 12) указывает на то, что пасвиная пленка теперь имеет повшенное содержание Cr (красная дария) по сравнению с Fe (черная сия) при соотноши. Ubuso budafite imbaraga kandi budafite imbaraga (Ishusho ya 12) bwerekana ko filime idakoresha imbaraga ubu ifite ingano ya Cr (umurongo utukura) yiyongereye ugereranije na Fe (umurongo w'umukara) ku gipimo cya Cr:Fe > 1.0.钝化和去皱表面（图 12 ）表明，钝化膜现在的 Cr （红线）含量高于 Fe （黑线）， Cr: Fe 比率> 1.0。 Cr （红线）含量高于 Fe （黑线）， Cr: Fe 比率> 1.0。 Пасси нововяя морщин няя поверхность (рис. 12) показывает, что пассивововяя пленка теперь имеет более всокое содержание Cr (красная дария), чем Фе (черная вия), при соотношении Cr. Ubuso budafite iminkanyari n'ubufite iminkanyari (Ishusho ya 12) bwerekana ko filime idakoresha iminkanyari ubu ifite Cr iri hejuru (umurongo utukura) kurusha Fe (umurongo w'umukara) ku gipimo cya Cr:Fe > 1.0.
Filimi ntoya (< 80 Å) irinda chromium oxide ikoresheje icyuma irinda kurusha filime ijana ya crystalline crystalline oxide iva mu cyuma cy’ibanze n’igipimo gifite icyuma kirenga 65%.
Imiterere y'ibinyabutabire by'ubuso budafite umwuka n'ubufite iminkanyari ubu igereranywa n'ibikoresho bisukuye bidakoresha umwuka. Umucanga mu rubanza rwa 1 ni umucanga wo mu cyiciro cya 2 ushobora gukorerwa aho uri; uko wiyongeranya, uduce duto duhinduka twimuka hamwe n'umwuka.
Muri iki gihe, ingese igaragara ntabwo izatera inenge zikomeye cyangwa kwangirika k'ubuso. Iminkanyari isanzwe izagabanya ingaruka zangiza ku buso kandi ikumire amahirwe yo kwimuka gukomeye kw'uduce dushobora kugaragara.
Ku Ishusho ya 11, ibisubizo bya AES bigaragaza ko urwego runini hafi y’ubuso rufite urugero rwo hejuru rwa Fe na O (500 Å ya okiside y’icyuma; imirongo y’icyatsi kibisi n’ubururu, uko bikurikirana), ruhinduka rukagera ku rugero rwa Fe, Ni, Cr, na O. Igipimo cya Fe (umurongo w’ubururu) kiri hejuru cyane kurusha icy’ikindi cyuma icyo ari cyo cyose, kiva kuri 35% ku buso kikagera kuri 65% mu cyuma.
Ku buso, urwego rwa O (umurongo w'icyatsi kibisi cyoroshye) ruva kuri hafi 50% mu gice cy'icyuma kivanze n'amazi kugera kuri zeru ku bugari bwa oxide film burenga 700 Å. Urugero rwa Ni (umurongo w'icyatsi kibisi wijimye) na Cr (umurongo utukura) ruri hasi cyane ku buso (< 4%) kandi ruriyongera kugera ku rugero rusanzwe (11% na 17%, uko bikurikirana) ku bujyakuzimu bw'icyuma. Urugero rwa Ni (umurongo w'icyatsi kibisi wijimye) na Cr (umurongo utukura) ruri hasi cyane ku buso (< 4%) kandi ruriyongera kugera ku rugero rusanzwe (11% na 17%, uko bikurikirana) ku bujyakuzimu bw'icyuma. Уровни Ni (темно-зеленая кария) и Cr (красная башия) чрезвинаайно низки на поверхности (<4%) и увеличиваются до Мазного оровня (11% и 17% соответственно) в глубине сплава. Urugero rwa Ni (umurongo w'icyatsi kibisi cyijimye) na Cr (umurongo utukura) ruri hasi cyane ku buso (<4%) kandi ruriyongera kugera ku rugero rusanzwe (11% na 17% uko bikurikirana) mu gice cy'amazi.Ni （深绿线）和 Cr （红线）水平极低（ <4% ），而在合金深度处增加到正常水平（分别为 11% 和 17% ）。Ni （深绿线）和 Cr （红线）水平极低（ <4% ），而在合金深度处增加到歌常水平（分别咺 11% Уровни Ni (темно-зеленая кария) и Cr (красная башия) на поверхности чрезвинаайно низки (<4%) и увеличиваются до Мазного оровня в глубине сплава (11% и 17% соответственно). Ingano ya Ni (umurongo w'icyatsi kibisi wijimye) na Cr (umurongo utukura) ku buso ni nto cyane (<4%) kandi yiyongera kugera ku rugero rusanzwe mu gice cy'ibumba (11% na 17% uko bikurikirana).
Ishusho ya AES iri ku ishusho ya 12 igaragaza ko urwego rwa rouge (okiside y'icyuma) rwakuweho kandi firime yo gusimbuka yasubiwemo. Mu urwego rw'ibanze rwa 15 Å, urwego rwa Cr (umurongo utukura) ruri hejuru y'urwego rwa Fe (umurongo w'umukara), ari na firime idasimbuka. Mu ntangiriro, ingano ya Ni ku buso yari 9%, yiyongeraho 60–70 Å hejuru y'urwego rwa Cr (± 16%), hanyuma izamuka ikagera ku rwego rwa alloy rwa 200 Å.
Guhera kuri 2%, urugero rwa karuboni (umurongo w'ubururu) rugabanuka kugera kuri zeru kuri 30 Å. Igipimo cya Fe mu ntangiriro kiba kiri hasi (< 15%) hanyuma kikangana n'igipimo cya Cr kuri 15 Å kandi gikomeza kwiyongera kikagera ku gipimo cy'ingufu ku kigero kirenga 65% kuri 150 Å. Igipimo cya Fe mu ntangiriro kiba kiri hasi (< 15%) hanyuma kikangana n'igipimo cya Cr kuri 15 Å kandi gikomeza kwiyongera kikagera ku gipimo cy'ingufu ku kigero kirenga 65% kuri 150 Å. Уровень Fe вначале низкий (<15%), позже равен оровню Cr при 15 Å и оололжает увеличиваться до оровня сплава более 65% при 150 Å. Igipimo cya Fe mu ntangiriro kiba kiri hasi (< 15%), nyuma kikaba kingana n'igipimo cya Cr kuri 15 Å kandi gikomeza kwiyongera kikagera ku gipimo cya alloy kirenga 65% kuri 150 Å. Fe 含量最初很低 (<15%) ，后来在 15 Å 时等于 Cr 含量，并在 150 Å 时继续增加到超过 65% 的合金含量。 Fe 含量最初很低 (<15%) ，后来在 15 Å 时等于 Cr 含量，并在 150 Å 时继续增加到超过 65% 的合金含量。 Содержание Fe изначально низкое (<15%), позже оно равняется содержанию Cr при 15 Å и продолжает увеличиваться до содержания сплава более 65% при 150 Å. Igipimo cya Fe mu ntangiriro kiba kiri hasi (< 15%), nyuma kikangana n'igipimo cya Cr kuri 15 Å kandi kigakomeza kwiyongera kugeza igihe igipimo cy'ibumba kirenze 65% kuri 150 Å.Igipimo cya Cr kiriyongera kigera kuri 25% by'ubuso kuri 30 Å kikagabanuka kigera kuri 17% mu gice cy'icyuma.
Igipimo cya O kiri hejuru hafi y'ubuso (umurongo w'icyatsi kibisi cyoroshye) kigabanuka kikagera kuri zeru nyuma y'ubujyakuzimu bwa 120 Å. Iri sesengura ryagaragaje filime yo gusohora ubuso yakozwe neza. Amafoto ya SEM ari ku ishusho ya 13 na 14 agaragaza imiterere y'ubuso bwa 1 n'ubwa 2 bwa oxide y'icyuma ikaze, ifunze kandi ifite imyenge. Ubuso bufunze bwerekana ingaruka za corruption ku buso bufunze igice (Ishusho ya 18-19).
Ubuso budafite aho buhuriye n'iminkanyari bugaragara ku ishusho ya 13 na 14 ntibushobora kwihanganira ogisijeni ikomeye. Ishusho ya 15 na 16 igaragaza firime yoroshye yo kudakoresha ku buso bw'icyuma.