| Ukukhethwa kwezinto ezifanelekileyo kulo naluphi na ulawulo okanye umgca wokujova ngekhemikhali kuxhomekeke kwiimeko zokusebenza ezikhoyo kunye nendawo. Ukuze kuncedwe ekukhetheni, ezi theyibhile zilandelayo zibonelela ngovavanyo loxinzelelo lwangaphakathi kunye nezinto zokulungisa uluhlu lweendidi eziqhelekileyo kunye nobukhulu beetyhubhu ezingenasici ezihlanganisiweyo nezihlanganisiweyo nge-laser. | ||||||||||
| Uxinzelelo oluphezulu (P) lwe-TP 316L kwi-100°F (38°C)1) | ||||||||||
| Nceda ujonge izinto ezingezantsi ezichaza umgangatho kunye nokulungiswa kwefom yemveliso. | ||||||||||
| Ububanzi obungaphandle, ngaphakathi. | Ubukhulu bodonga, ngaphakathi. | Uxinzelelo lokusebenza2) | Uxinzelelo oluqhumayo2) | Uxinzelelo lokugoba4) | ||||||
| i-psi (MPa) | i-psi (MPa) | i-psi (MPa) | ||||||||
| 1/4 | 0.035 | 6,600 (46) | 22,470 (155) | 6,600 (46) | ||||||
| 1/4 | 0.049 | 9,260 (64) | 27,400 (189) | 8,710 (60) | ||||||
| 1/4 | 0.065 | 12,280 (85) | 34,640 (239) | 10,750 (74) | ||||||
| 3/8 | 0.035 | 4,410 (30) | 19,160 (132) | 4,610 (32) | ||||||
| 3/8 | 0.049 | 6,170 (43) | 21,750 (150) | 6,220 (43) | ||||||
| 3/8 | 0.065 | 8,190 (56) | 25,260 (174) | 7,900 (54) | ||||||
| 3/8 | 0.083 | 10,450 (72) | 30,050 (207) | 9,570 (66) | ||||||
| 1/2 | 0.049 | 4,630 (32) | 19,460 (134) | 4,820 (33) | ||||||
| 1/2 | 0.065 | 6,140 (42) | 21,700 (150) | 6,200 (43) | ||||||
| 1/2 | 0.083 | 7,840 (54) | 24,600 (170) | 7,620 (53) | ||||||
| 5/8 | 0.049 | 3,700 (26) | 18,230 (126) | 3,930 (27) | ||||||
| 5/8 | 0.065 | 4,900 (34) | 19,860 (137) | 5,090 (35) | ||||||
| 5/8 | 0.083 | 6,270 (43) | 26,910 (151) | 6,310 (44) | ||||||
| 3/4 | 0.049 | 3,080 (21) | 17,470 (120) | 3,320 (23) | ||||||
| 3/4 | 0.065 | 4,090 (28) | 18,740 (129) | 4,310 (30) | ||||||
| 3/4 | 0.083 | 5,220 (36) | 20,310 (140) | 5,380 (37) | ||||||
| 1) Uqikelelo kuphela. Uxinzelelo lokwenyani kufuneka lubalwe kujongwa zonke izinto ezibangela uxinzelelo kwinkqubo. | ||||||||||
| 2) Ngokusekelwe kubalo oluvela kwi-API 5C3, kusetyenziswa ukunyamezelana kodonga kwe-+/-10% | ||||||||||
| 3) Ngokusekelwe kwiindlela zokubala ezikhawulezayo zokuqhuma kwamandla ezivela kwi-API 5C3 | ||||||||||
| 4) Ngokusekelwe kwizibalo zokuwa kwe-yield strength collapses ezivela kwi-API 5C3 | ||||||||||
| Izinto zohlengahlengiso kwimida yoxinzelelo lokusebenza1) | ||||||||||
| I-Pw = umlinganiselo woxinzelelo olusebenzayo olubhekisele kwi-TP 316L kwi-100°F (38°C). Ukufumanisa uxinzelelo olusebenzayo lokudibanisa inqanaba/ubushushu, phinda-phinda i-Pw nge-adjustment factor. | ||||||||||
| Ibanga | 100°F | 200°F | 300°F | 400°F | ||||||
| (38)°C) | (93)°C) | (149)°C) | (204)°C) | |||||||
| I-TP 316L, ayinamthungo | 1 | 0.87 | 0.7 | 0.63 | ||||||
| I-TP 316L, idityanisiwe | 0.85 | 0.74 | 0.6 | 0.54 | ||||||
| I-alloy 825, ayinamthungo | 1.33 | 1.17 | 1.1 | 1.03 | ||||||
| I-alloy 825, edityanisiweyo | 1.13 | 1.99 | 1.94 | 0.88 | ||||||
| 1) Izinto zokulungisa ezisekelwe kuxinzelelo oluvumelekileyo kwi-ASME. | ||||||||||
| Izinto zokulungisa imida yoxinzelelo oluqhumayo1) | ||||||||||
| I-Pb = uxinzelelo lokuqhuma olubhekisele kwi-TP 316L kwi-100°F. Ukufumanisa uxinzelelo lokuqhuma komxube webanga/ubushushu, phinda-phinda i-Pb nge-adjustment factor. | ||||||||||
| Ibanga | 100°F | 200°F | 300°F | 400°F | ||||||
| (38)°C) | (93)°C) | (149)°C) | (204)°C) | |||||||
| I-TP 316L, ayinamthungo | 1 | 0.93 | 0.87 | 0.8 | ||||||
| I-TP 316L, idityanisiwe | 0.85 | 0.79 | 0.74 | 0.68 | ||||||
| I-alloy 825, ayinamthungo | 1.13 | 1.07 | 1 | 0.87 | ||||||
| I-alloy 825, edityanisiweyo | 0.96 | 0.91 | 0.85 | 0.74 | ||||||
| 1) Izinto zokulungisa ezisekelwe kumandla okugqibela kwi-ASME. | ||||||||||