It adheres on the tenet “Honest, industrious, enterprising, innovative” to acquire new solutions regularly. It regards shoppers, success as its very own success. Let us establish prosperous future hand in hand for Factory made hot-sale Cold Rolled And Hot Rolled 316l Stainless Steel Coil Low 316l Stainless Steel Coil, At our firm with good quality initially as our motto, we manufacture merchandise that are entirely made in Japan, from materials procurement to processing. This enables them for being used with confident peace of mind.
It adheres on the tenet “Honest, industrious, enterprising, innovative” to acquire new solutions regularly. It regards shoppers, success as its very own success. Let us establish prosperous future hand in hand for 316l Stainless Steel Coil, Hot Rolled 316l Stainless Steel Coil, Low 316l, We also have the strong ability of integration to supply our best service, and plan to build the warehouse in the different countries around the world, that will likely be more conveniently to service our customers.
General Properties

Alloy 304L a T-300 series stainless steel austenitic, which has a minimum of 18% chromium and 8% nickel. Type 304L has a carbon maximum is 0.030. It is the standard “18/8 stainless” that is commonly found in pans and cooking tools. Alloys 304L is the most versatile and widely used alloy in the stainless steel family. Ideal for a wide variety of home and commercial applications, Alloys 304L exhibits excellent corrosion resistance and has a high ease of fabrication, outstanding formability. The austenitic stainless steels are also considered to be the most weldable of the high-alloy steels and can be welded by all fusion and resistance welding processes.

Specifications:  UNS S30403

Applications:

Alloy 304L Stainless Steel is used in a wide variety of home and commercial applications, including:

Food processing equipment, particularly in beer brewing, milk processing, and wine making

Kitchen benches, sinks, troughs, equipment, and appliances

Architectural trim and molding

Automotive and aerospace structural use

Construction material in large buildings

Chemical containers, including for transport

Heat exchangers

Nuts, bolts, screws, and other fasteners in the marine environment

Dyeing industry

Woven or welded screens for mining, quarrying & water filtration

Standards:

ASTM/ASME:  S30403

EURONORM:  1.4303

AFNOR:  Z2 CN 18.10

DIN:  X2 CrNi 19 11

Corrosion Resistance:

Resistance to corrosion in oxidizing environments is a result of the 18 to 19% chromium that the 304 alloys contain.

Resistance to moderately aggressive organic acids is a result of the 9 to 11% nickel that the 304 alloys contain.

At times, alloy 304L may show a lower corrosion rate than the higher carbon Alloy 304; otherwise, the 304, 304L, and 304H may be considered to perform uniformly in most corrosive environments.

Alloy 304L is preferred for use in environments sufficiently corrosive to cause intergranular corrosion of welds and heat-affected zones on susceptible alloys.

Heat Resistance:

Good oxidation resistance in intermittent service to 1600°F and in continuous service to 1690°F.

Continuous use of 304 in the 800-1580°F range is not recommended if subsequent aqueous corrosion resistance is important.

Grade 304L is more resistant to carbide precipitation and can be heated into the above temperature range.

Properties of 304 Alloy

Welding Characteristics:

Excellent welding properties; post-weld annealing is not required when welding thin sections. Two important considerations in producing weld joints in the austenitic stainless steels are:

preservation of corrosion resistance

avoidance of cracking

Processing – Hot Forming:

To forge, heat uniformity to 2100 / 2300 °F

Do not forge below 1700 °F

Forging can be air cooled without danger of cracking

Processing – Cold Forming:

Its austenitic structure allows it to be deep-drawn without intermediate annealing, Making this the stainless steel grade of choice in the manufacturing of sinks, hollow-ware and saucepans.

These grades work harden rapidly. To relieve stresses produced in severe forming or spinning, parts should be full annealed or stress relief annealed as soon as possible after forming.

Machinability:

The use of chip breakers is advised since the chips can be stringy. Stainless steel work harden rapidly, heavy positive feeds, sharp tooling, and a rigid set-up should be used.of cut below the work-hardened layer resulting from the previous passes.

Chemical Properties:

Mechanical Properties:

Physical Properties:

Surface treatment

Stainless steel  international standard:

INTERNATIONAL  STANDARD: